STRUCTURAL EVALUATION OF Mg-ADDED SINGLE-CHAIN 1.1nm TOBERMORITE BY LOW-PRESSURE WATER VAPOR ADSORPTION

DOI Web Site 7 References
  • ISHIYAMA Nachi
    NIIGATA UNIVERSITY, Graduate School of Science and Technology（8050, Ikarashi Ninocho, Nishi-ku, Niigata-shi, Niigata 950-2181, Japan）
  • SAITO Tsuyoshi
    NIIGATA UNIVERSITY, Faculty of Engineering（8050, Ikarashi Nino-cho, Nishi-ku, Niigata-shi, Niigata 950-2181, Japan）
  • SUZUKI Kazuho
    NIIGATA UNIVERSITY, Graduate School of Science and Technology（8050, Ikarashi Ninocho, Nishi-ku, Niigata-shi, Niigata 950-2181, Japan）
  • MATSUI Kunio
    ASAHIKASEI HOMES（2-1, Sameshima, Fuji-shi, Shizuoka 416-0934, Japan）

Bibliographic Information

Other Title
  • 低圧水蒸気吸着によるMg添加した単鎖型1.1nmトバモライトの構造評価

Abstract

<p>This paper reports on the evaluation interlayer structure of a sample transformed from 1.4nm Tobermorite to 1.1nm Tobermorite with a single chain structure by heat treatment using the isosteric heat of water adsorption calculated from low-pressure water vapor adsorption isotherms. In the isosteric heat of adsorption, there was a difference in the appearance of peaks between the tobermorite and C-S-H samples, suggesting that the regularity of the crystal structure and the uniformity of the Si chain structure affect the bimodal peaks in the heat of adsorption. In addition, an increase in the heat of adsorption was observed in the Mg-added sample, which was attributed to the high-water content and high hydration energy of Mg2＋ ions.</p>