Fabrication of Low-Density-Polyetylene-Based Transparent Hygroscopic Resin Dispersed with Nano-Sized Zeolite
-
- Takamitsu KAKINAGA
- Nakamura Choukou Co., Ltd.
-
- Toru WAKIHARA
- Graduate School of Engineering, The University of Tokyo
-
- Atsushi NAKAHIRA
- 3rd Cluster, Material Sci. and Eng., Osaka Metropolitan University
-
- Hidenobu MURATA
- 3rd Cluster, Material Sci. and Eng., Osaka Metropolitan University
この論文をさがす
抄録
<p>In order to realize transparent and hygroscopic films, it was shown that transparent hygroscopic films could be realized by surface modification of 4A zeolite with a median diameter of 50 nm to bring the refractive indices of the EVA resin and zeolite closer together. In order to make this technology applicable to general purpose, LDPE or LLDPE is suited as the base resin, and thin films should be produced by the inflation method. In this study, we attempted to realize a transparent moisture-absorbing film with LLDPE as the resin material and 50% nano-sized zeolite addition. However, the higher the zeolite content, the more difficult kneading and film-forming processes become. In fact, by using the blown film extrusion and cast film extrusion processes, it was impossible to form a film by tearing after extrusion when film processing was attempted by adding nano-sized zeolite with a surface modification treatment that produces high transparency. The results of our attempts to improve the problems from these results, it was found that a combination of a surface modifier that is highly effective in increasing the refractive index of the particles to increase their transparency and a modifier with excellent processability can be useful to facilitate kneading and molding. As a result, it was confirmed that resins containing 50 wt% surface-modified zeolite with such two surface modifiers could form 30 micrometer-thick films without dilution.</p>
収録刊行物
-
- 材料
-
材料 72 (10), 743-749, 2023-10-15
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390016372308393472
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 033123080
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
-
- 抄録ライセンスフラグ
- 使用不可