生型ばい焼再生砂によるシェル鋳型強度の阻害に及ぼすベントナイトの影響

DOI

書誌事項

タイトル別名
  • Effect of Bentonite on Strength Inhibition of Shell Mold using Recycled Calcination Sand from Green Sand Molds

抄録

<p>  We investigated the reasons for why shell mold strength decreases when green sand is reclaimed by calcination at lower temperatures. When calcination is performed at temperatures above 740℃, the shell mold strength increases. The temperature of 740℃ is close to the OH group dehydration temperature for bentonite, which is present below 740℃, and is thought to reduce shell mold strength. To investigate this relationship, we added bentonite to shell mold sand, and confirmed that it reduces the shell mold strength. Using scanning electron microscopy, we found that bentonite prevents resin adhesion to sand particles and causes embrittlement of the resin coating. Moreover, the results of gel-permeation chromatography and powder X-ray diffraction analysis indicated that intercalation of bentonite in the phenolic resin reduces shell mold strength.</p>

収録刊行物

  • 鋳造工学

    鋳造工学 95 (11), 600-607, 2023-11-25

    公益社団法人 日本鋳造工学会

キーワード

詳細情報 詳細情報について

  • CRID
    1390016880929565824
  • DOI
    10.11279/jfes.95.600
  • ISSN
    21855374
    13420429
  • 本文言語コード
    ja
  • データソース種別
    • JaLC
  • 抄録ライセンスフラグ
    使用不可

問題の指摘

ページトップへ