Liquid-Phase Diffusion Bonding of Al alloy for Casting Using Formate Coated Insert Sheet
-
- KOYAMA Shinji
- Graduate School of Engineering, Gunma University
-
- SHINOHARA Yuto
- Graduate School of Engineering, Gunma University (Present affiliation: TOSHIBA CORPORATION)
Bibliographic Information
- Other Title
-
- ギ酸塩被膜付与インサート材を用いた鋳造用Al合金の液相拡散接合
Abstract
Liquid-phase diffusion bonding was performed in air at a bonding temperature of 400°C, a bonding pressure of 20 MPa, and a heat holding time of 15 min. The specimens for liquid-phase diffusion bonding were AC2C and ADC12, aluminum alloy for casting. After liquid-phase diffusion bonding, solution annealing and aging treatments were also performed on the joints. As a result, the joint strength was improved by about 2 times and the joint efficiency was 90% by using the 3-layer insert material as compared with the Zn single-layer insert material. This was because the Si concentration in the liquid phase decreased by using the 3-layer insert material and Si was discharged to the outer circumference of the joint. By using the 3-layer insert material, the interfacial fracture factor after T6 heat treatment changed from Si particles to Mg oxides.
Journal
-
- QUARTERLY JOURNAL OF THE JAPAN WELDING SOCIETY
-
QUARTERLY JOURNAL OF THE JAPAN WELDING SOCIETY 41 (4), 364-370, 2023
JAPAN WELDING SOCIETY
- Tweet
Details 詳細情報について
-
- CRID
- 1390017193112206208
-
- ISSN
- 24348252
- 02884771
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- Crossref
-
- Abstract License Flag
- Disallowed