炭素固溶チタン焼結押出材の結晶組織と強化機構

DOI Web Site Web Site 参考文献17件

書誌事項

タイトル別名
  • Microstructure and Strengthening Mechanism of Powder Metallurgy Extruded Titanium Alloys with Carbon Solid Solution
  • タンソコヨウ チタン ショウケツ オシダシザイ ノ ケッショウ ソシキ ト キョウカ キコウ

この論文をさがす

説明

<p>The effect of carbon elements on the microstructures and mechanical properties of pure Ti alloys fabricated through extruded powder metallurgy route was investigated. Furthermore, the strengthening mechanism of extruded materials was also investigated quantitatively. In Ti-C materials, the lattice parameter in c-axis of α-Ti increased due to solid solution of carbon atoms in the most stable octahedral interstitial sites. As the carbon contents increased, tensile strength was increased while maintaining a high elongation at break. The 0.2% yield stress of Ti-2.0 mass% TiC increased by 242 MPa compared with pure Ti. The elongation at break value exceeded 35.0% for all specimens. According to this analysis, it was clarified that Fm value of Ti-C materials was 2.90 × 10-10 by using Labusch model. The estimated strengthening improvement using these values was significantly agreed with the experimental results of PM Ti alloys with carbon solution atoms. Furthermore, the strengthening mechanism of the alloys was quantitatively clarified that carbon solution strengthening was the dominant factor in this study.</p>

収録刊行物

参考文献 (17)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ