Fluorometric determination of trace amount of gallium in high-purity aluminum with 2- hydroxy-5-sulfoaniline-<I>N</I>-salicylidene
-
- WADA Kazuhito
- Faculty of Engineering, Hiroshima University
-
- MORISHIGE Kiyotoshi
- Faculty of Science and Technology, Kinki University
-
- YAMAGUCHI Kenji
- Hiroshima City Art and Industry Institute
Bibliographic Information
- Other Title
-
- 2‐ヒドロキシ‐5‐スルホニリン‐N‐サリチリデンによる高純度アルミニウム中の微量ガリウムのけい光定量
- 2 ヒドロキシ 5 スルホアニリン N サリチリデン ニ ヨル コウ ジュンド
- 2-ヒドロキシ-5-スルホアニリン-N-サリチリデンによる高純度アルミニウム中の微量ガリウムの蛍光定量
Search this article
Abstract
The procedure was as follows : 0.10.2g of a sample containing less than 20 μg of gallium was dissolved by heating in 5 ml of hydrochloric acid (2+1). To the solution obtained, were added 0.1 ml of 20 % titanium trichloride solution and 5 ml of hydrochloric acid(2+1). The gallium in the solution was extracted twice with 5 ml each of isopropylether by shaking for 1 min. The organic phase was washed 5 times with 2 ml each of hydrochloric acid(2+1) by shaking for 15 s. The organic phase was evaporated to dryness on a water bath, and the residue was dissolved in 2 ml of hydrochloric acid (1+100) and diluted to 10 ml with water. To an aliquot containing 0.0053.0μg of gallium, were added 0.1 % sodium fluoride solution (Ga<0.1μg : 0.05 ml, Ga> 0.1μg : 0.1 ml), 2 ml of 0.05 % HSS solution in DMF and 0.5 ml of 2 w/v % ammonium acetate solution. The pH of the solution was adjusted to 3.8±0.1 with hydrochloric acid or ammonia water, and the solution was diluted to 25 ml with water. The solution was heated at 50°C for 10 min in a water bath. After cooling to room temperature, the fluorescence intensity was measured at 500 nm (λ excitation : 410 nm) against the standard uranine solution (0.05 μg/m1 or 0.2 μg/ml). The proposed method could be applied to the determination of gallium above 0.05 ppm in practical samples with satisfactory results.
Journal
-
- BUNSEKI KAGAKU
-
BUNSEKI KAGAKU 33 (4), 223-226, 1984
The Japan Society for Analytical Chemistry
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282679029527680
-
- NII Article ID
- 110002908914
-
- NII Book ID
- AN00222633
-
- NDL BIB ID
- 2984360
-
- ISSN
- 05251931
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- NDL-Digital
- CiNii Articles
-
- Abstract License Flag
- Disallowed