ばら積石炭船倉内の腐食を模擬した希硫酸環境における造船用鋼の腐食および腐食疲労

DOI NDLデジタルコレクション Web Site 被引用文献1件 参考文献16件

書誌事項

タイトル別名
  • Corrosion and Corrosion Fatigue of a Ship Structural Steel in Dilute Sulfuric Acids Substituted for a Corrosion Environment of a Coal Cargo Hold
  • バラヅミ セキタン センソウ ナイ ノ フショク オ モギ シタ キリュウサン カンキョウ ニ オケル ゾウセンヨウ コウ ノ フショク オヨビ フショク ヒロウ ガン トウロン

この論文をさがす

抄録

An acid corrosive environment of a coal cargo hold was reproduced experimentally by using immersions of coal. Immersion tests, crack growth tests, and corrosion fatigue tests were performed under dilute sulfuric acids on a ship structural steel plate.<BR>A pH decreased with passage of time in an exudation solution from coal, and the end point was pH 2. 5. Corrosion rates were obtained in exudation solution and in dilute sulfuric acids of pH 4, pH 3 and pH 2. It could be confirmed that the corrosion rate in a dilute sulfuric acid could be substituted for that in the exudation solution from coal.<BR>The conditions of the fatigue crack initiation, ΔKCF, were obtained from the observations of corrosion pits by a scanning electron microscope. The ΔKCF was 3.60 and 5.39 MPa m1/2 in H2SO4 at pH 4 and at pH 2, respectively. The crack growth rates estimated under corrosive dissolutions were 5.63 × 10-10 and 1.90 × 10 -9m/cycle for ΔKCF in above environments. Concerning corrosion fatigue, S/ N curves, Seq/Nc curves on modified MIL HDBK 5 and ΔK/Nc curves were discussed in comparison with corrosion fatigue in seawater.

収録刊行物

被引用文献 (1)*注記

もっと見る

参考文献 (16)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ