- Effects of MnS Inclusion and the Potentiostatic Etching Treatment on Pitting Corrosion Resistance of 18-8 Stainless Steels.
- 18-8 ステンレス コウ ノ タイ コウショクセイ ニ オヨボス MnS カ
この論文をさがす
説明
The effects of MnS inclusions and of electrolytic treatment in the active and passive region on the pitting resistance of 18-8 stainless steels have been studied in 3%NaCl solution mainly by electrochemical means. The pitting resistance of the specimens depended on the electrolytic potential. In the specimens electrolyzed in the active region directly below the passivation potential, pitting potential had a tendency to become noble, and this tendency was pronounced in specimen containing a small quantity of MnS or having a small Mn/S ratio. Cr concentration on the steel surface was increased by the electrolytic treatment, and the concentration had a tendency to inrease as electrolytic potential became more noble. Although there appears to be little correlation between Cr concentration and pitting potential, there does appear to be a correlation between the morphology of corrosion and the pitting potential. That is to say, electrolyzing just below the passivation potential at which dissolution of the matrix and MnS occure, let to greatly improve pitting resistance. This was due to the dissolution of MnS, which acts as the pit initiation site, and to Cr enrichment on the steel surface, which occurrs simultaneously.
収録刊行物
-
- 表面技術
-
表面技術 42 (6), 649-654, 1991
一般社団法人 表面技術協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679090592768
-
- NII論文ID
- 130001073183
-
- NII書誌ID
- AN1005202X
-
- COI
- 1:CAS:528:DyaK3MXmsVansbY%3D
-
- ISSN
- 18843409
- 09151869
-
- NDL書誌ID
- 3720932
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可