塩酸溶液中でのチタンとチタン-パラジウム合金の接触腐食
書誌事項
- タイトル別名
-
- Galvanic Corrosion between Titanium and a Titanium-Palladium Alloy in Hydrochloric Acid
この論文をさがす
説明
Galvanic corrosion between titanium and a titanium-palldium alloy was studied by measuring the polarization characteristics and the weight loss by dipping in 0.5-1.0N HCl at 90°C. The following results were obtained: (1) When titanium was contacted with a titanium-palladium alloy, the corrosion rates of the both metals were almost the same at any concentration of HCl. When the concentration was 7N or higher, their corrosion rates were higher than that of titanium alone in HCl. (2) An active behavior was observed in the anodic polarization curve of titanium when the concentration of HCl was not lower than 1N, but the behavior was not observed in the alloy when the concentration was up to 8N. The coupled potential of titanium and the alloy was at a potential nobler than the critical potential for passivation of titanium in a dilute HCl up to about 3N. When the concentration was increased to 6-7N, the coupled potential was in the incomplete passivation region. When the concentration was 7N or higher, the coupled potential was at the peak current of passivation.
収録刊行物
-
- 金属表面技術
-
金属表面技術 24 (8), 433-436, 1973
一般社団法人 表面技術協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679090643840
-
- NII論文ID
- 130003994062
-
- ISSN
- 18843395
- 00260614
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可