亜鉛めっき鋼板上へのりん酸アルミニウム熱重合体皮膜の形成について

DOI

書誌事項

タイトル別名
  • Formation of Thermally Polymerized Aluminum Phosphate Films on Zinc-Plated Steel Sheets

抄録

A new chemical conversion coating process using aluminum biphosphate has been proposed, and the film formation behavior and mechanism of thermally polymerized aluminum phosphate have been studied. The chemical conversion film formed by heating the aluminum biphosphate coating on zinc-plated steel sheets provides good protection against corrosion. Reaction for the film formation is a condensation polymerization caused by the dehydration of bound water in aluminum biphosphate. The experimental results obtained by using DSC, TGA, IR spectrometry and X-ray diffractometry showed that the dehydration at about 150°C is most important to form the anticorrosive film. Accordingly, for the production of the chemically converted film it is required to heat up to at least about 180°C, at which most of the dehydration reaction ends. However, the dehydration and hydration of the film occured reversibly. The reason for this rehydration is assumed that thermally polymerized film possesses a non-stoichiometrical aluminum phosphate structure.

収録刊行物

  • 金属表面技術

    金属表面技術 28 (6), 336-340, 1977

    一般社団法人 表面技術協会

詳細情報 詳細情報について

  • CRID
    1390282679090883328
  • NII論文ID
    130003994260
  • DOI
    10.4139/sfj1950.28.336
  • ISSN
    18843395
    00260614
  • 本文言語コード
    ja
  • データソース種別
    • JaLC
    • Crossref
    • CiNii Articles
  • 抄録ライセンスフラグ
    使用不可

問題の指摘

ページトップへ