- Corrosion Wear of Alloy Tool Steel(SKD11) Coated with VC and Precipitation Hardening Stainless Steel(SUS630) in Sodium Chloride Aqueous Solution.
- VC デ ヒフクシタ ゴウキン コウグ コウ SKD 11 オヨビ セキシュツ
この論文をさがす
抄録
We studied corrosion wear of alloy tool steel (SKD 11) coated with VC and precipitation-hardened stainless steel (SUS 630) in NaCl aqueous solution. SUS 630 lost more weight than SKD 11 coated with VC, except where SUS 630 was used as a rotor at a load region below 9.8×10-1MPa. VC film appeared externally sound overall. Sample edges revealed galvanic corrosion of the substrate and partial disappearance of the VC film, and SUS 630 was plastically deformed under high load. The polarization curve indicated that VC film and SUS 630 form a galvanic couple with SKD 11 in NaCl solution, and that VC film and SUS 630 behave cathodic and SKD 11 anodic.<br>Pinhole defects were detected in VC-coated SKD 11 using optical and scanning electron microscopy by anodic polarization in deaerated 0.5kmol·m-3 H2SO4 solution. Pinhole defects averaged 2∼4 per cm2
収録刊行物
-
- 表面技術
-
表面技術 47 (6), 536-542, 1996
一般社団法人 表面技術協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679091192704
-
- NII論文ID
- 10002256590
-
- NII書誌ID
- AN1005202X
-
- ISSN
- 18843409
- 09151869
-
- NDL書誌ID
- 3976398
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可