リン酸‐酸化鉄‐ＰＶＢ系さび安定化処理膜のイオン選択透過性と安定さび生成機構

DOI Web Site 参考文献8件

書誌事項

タイトル別名
  • Ion Selectivity and Mechanism of Stable Rust Formation of Phosphoric Acid-Iron Oxide-PVB Rust Stabilization Surface Treatment Film.
  • リンサン サンカ テツ PVBケイサビ アンテイカ ショリ マク ノ イオン

この論文をさがす

抄録

Despite thier thinness, films applied to weathering steel using a phosphoric acid-iron oxide-PVB rust stabilization surface treatment act to inhibit rust formation and to suppress“rust outflow”. The following conclusions were reached in a study of the reasons for the treatment's effectiveness.<br>(1) The treatment film exhibits cation selectivity in a NaCl solution and KCl solution and anion selectivity in a FeCl2 solution and FeCl3 solution. Accordingly, by acting to suppress the diffusion of Cl-, Fe2+ and Fe3+, the film inhibits corrosion of the iron matrix and the occurrence of“rust out-flow”.<br>(2) Examination of artificial rust (amorphous rust) revealed that a compound layer comprised of the treatment film and rust acts as a bipolar film with both cation selectivity and anion selectivity. The compound layer also suppresses the diffusion of Cl-, Fe2+ and Fe3+.<br>(3) Because the treatment film has a relatively high permeability for moisture and oxygen, PO43- and other phosphate ions easily flow out of the film during prolonged atmospheric exposure. It is thought that PO43-, in addition to imparting ion selectivity to the rust, contributes, together with the alloying elements, to rust stabilization in weathering steel.

収録刊行物

  • 表面技術

    表面技術 47 (4), 366-371, 1996

    一般社団法人 表面技術協会

参考文献 (8)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ