ホウ酸硫酸混合電解液を用いるアルミニウムの陽極酸化とホウ素含有量

DOI Web Site オープンアクセス

書誌事項

タイトル別名
  • Morphology and Boron Content of Anodic Aluminum Oxide Films Formed in Boric/Sulfuric Acid Baths.
  • ホウサン リュウサン コンゴウ デンカイエキ オ モチイル アルミニウム ノ
公開日
1994
DOI
  • 10.4139/sfj.45.1152
公開者
一般社団法人 表面技術協会

この論文をさがす

説明

The boric/sulfuric acid anodizing process has been developed in the U. S. as a replacement for chromic acid anodizing to meet stricter environmental regulations. A comparative study has been conducted on the microstructures of boric/sulfuric acid films and sulfuric acid films. The sulfur and boron contents of the oxide films were determined by prompt gamma ray analysis. The type of V-t and I-t curves, and the morphology of pores were not appreciably influenced by the presence of boric acid in the anodizing bath, but the rate of formation of the boric/sulfuric acid films increased slightly and the rate of their disolution in phosphoric acid solution decreased slightly. The concentration of boric acid did not influence the amount of surfur incorporated into the oxide films. After the pores were sealed, surfur content decreased significantly due to the dissolution of sulfur compounds to the sealing solution.<br>The boron content of porous type films was negligible, in the order of ppm. This is in remarkable contrast to the barrier type films formed in borate solutions, where boron contents of the order of several per cent have been reported. The boron content increased with increasing concentration of boric acid in the electrolytes.

収録刊行物

  • 表面技術

    表面技術 45 (11), 1152-1157, 1994

    一般社団法人 表面技術協会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ