- Fabrication of Amorphous Fe-B Alloy Films by Contact Plating Method and Their Magnetic Properties.
- セッショクメッキ ホウ ニ ヨル Fe-B2ゲンケイ アモルファス ゴウキン
この論文をさがす
抄録
Fe-B amorphous alloy film was formed by means of contact plating method, in which Cu foils in contact with Al wires were used as substrates. Local battery configuration of the Cu foil anode and the Al wire cathode was responsible for film formation. The boron content in film was controlled from 0at% to 28at% by changing the KBH4 concentration in the bath. The bath temperature strongly affected the crystallographic structure of resultant films. Fe80B20 amorphous films required a bath temperature below 40°C. Film structure and composition also affected magnetic properties. Film coercivity below 17Oe was also observed.
収録刊行物
-
- 表面技術
-
表面技術 49 (7), 769-774, 1998
一般社団法人 表面技術協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679092179584
-
- NII論文ID
- 10002110011
-
- NII書誌ID
- AN1005202X
-
- COI
- 1:CAS:528:DyaK1cXksFOnsbY%3D
-
- ISSN
- 18843409
- 09151869
- http://id.crossref.org/issn/09151869
-
- NDL書誌ID
- 4514780
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可