シュウ酸浴からのAl<sub>2</sub>O<sub>3</sub>複合Cr-C合金めっき

DOI Web Site Web Site 参考文献1件

書誌事項

タイトル別名
  • Electrodeposition of Al<sub>2</sub>O<sub>3</sub> Composite Cr-C Alloy Coatings from Oxalic Bath
  • シュウ酸浴からのAl₂O₃複合Cr-C合金めっき
  • シュウサンヨク カラ ノ Al ₂ O ₃ フクゴウ Cr-C ゴウキンメッキ

この論文をさがす

抄録

<p>Electrodeposited Al2O3 composite Cr-C alloy coatings were produced from an oxalic acid bath prepared by adding oxalic acid to a hot CrO3 solution. Chromium ions in the oxalic bath include Cr3＋ oxalate complex and Cr6＋ ions. The Al2O3 particles were co-deposited easily along with the Cr-C alloy coating from the oxalic bath. The content was controlled up to about 3 wt% by plating conditions. The Al2O3 contents of the coatings decreased with current density and increased with bath temperature. The added amount of oxalic acid at make-up of the bath increased the Al2O3 contents of the coatings. The co-deposition mechanism was supported with a two-step adsorption mechanism proposed by Guglielmi, but the adsorption of Al2O3 tothe cathode in the oxalic bath was much weaker than that of either Ni composite plating or Cr composite plating.</p>

収録刊行物

  • 表面技術

    表面技術 67 (12), 685-688, 2016

    一般社団法人 表面技術協会

参考文献 (1)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ