Electrochemical Impedance Analysis for Electrochemical Migration of Screen-printed Silver Wiring Electrodes
-
- SHITANDA Isao
- Faculty of Science and Technology, Tokyo University of Science
-
- YAMAMOTO Katsuhiro
- Faculty of Science and Technology, Tokyo University of Science
-
- WATANABE Kunihiro
- Faculty of Science and Technology, Tokyo University of Science
-
- ITAGAKI Masayuki
- Faculty of Science and Technology, Tokyo University of Science
-
- ASANO Yasufumi
- R&D Section, Newlong Seimitsu Kogyo Co., Ltd.
Bibliographic Information
- Other Title
-
- スクリーン印刷で形成した銀配線におけるエレクトロケミカルマイグレーションの電気化学インピーダンス評価
- スクリーン インサツ デ ケイセイ シタ ギン ハイセン ニ オケル エレクトロケミカルマイグレーション ノ デンキ カガク インピーダンス ヒョウカ
Search this article
Abstract
Electrochemical migration processes on two screen-printed silver wiring electrodes were investigated using electrochemical impedance spectroscopy. The impedance measured immediately after initial growth of silver dendrites on the cathode shows three capacitive loops. A loop in the low frequency range was dependent on the electric double layer capacitance and reaction resistance of electrodeposition of silver and oxygen reduction on the cathode. The capacitive loop diameter in the low frequency range decreased with dendrite growth. A capacitive loop in the middle frequency range was attributed to the dissolution reaction of silver on the anode. Results showed that a capacitive loop in the high-frequency range was related to the interelectrode capacitance between the silver wiring electrodes and the water film’s solution resistance. Curve fitting was performed for the impedance spectra by assuming an equivalent circuit. The calculated impedance spectra showed good agreement with experimental results: the reaction resistances and double layer capacitances varied remarkably with dendrite generation, suggesting that the present silver wiring electrode is applicable to an electrochemical migration monitoring sensor.
Journal
-
- Journal of The Surface Finishing Society of Japan
-
Journal of The Surface Finishing Society of Japan 60 (5), 342-348, 2009
The Surface Finishing Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390282679095576064
-
- NII Article ID
- 10025395277
-
- NII Book ID
- AN1005202X
-
- COI
- 1:CAS:528:DC%2BD1MXmtlygs7s%3D
-
- ISSN
- 18843409
- 09151869
-
- NDL BIB ID
- 10294899
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed