- Initial Corrosion Behavior of Carbon Steel under a Thin Electrolyte Layer Using a Multi-Monitoring System
- タイキ フショク マルチ モニタリング システム ニ ヨル エキ ハクマク カ デ ノ タンソ コウ ノ ショキ フショク キョドウ
この論文をさがす
説明
A multi-monitoring system has been constructed to research atmospheric corrosion behavior of metal continuously and multifariously. The system consists of a microscope, a surface potential apparatus, a corrosion monitor and a chamber which can control both temperature and relative humidity. Initial corrosion behavior of carbon steel under a thin electrolyte layer has been studied using this system. As the result of monitoring of impedance and surface potential for relative humidity, the surface potential shifted to less noble and the corrosion rate increased with an increase of relative humidity. Furthermore, the change in the surface potential and corrosion rate for the average thickness of a thin electrolyte layer calculated thermodynamically has been researched. The surface potential shifted to noble with a decrease of electrolyte layer thickness, and the corrosion rate showed a maximum at a thickness of about 80 μm. Based on the results of surface potential and corrosion rate, the initial corrosion behavior of carbon steel under a thin electrolyte layer has been discussed.
収録刊行物
-
- 表面技術
-
表面技術 54 (12), 1022-1027, 2003
一般社団法人 表面技術協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679095800448
-
- NII論文ID
- 10011819442
-
- NII書誌ID
- AN1005202X
-
- COI
- 1:CAS:528:DC%2BD2cXhvFWmtrs%3D
-
- ISSN
- 18843409
- 09151869
-
- NDL書誌ID
- 6817021
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可