Polyaniline/Silica Hybrid Gels Prepared by Catalytic Polymerization Using Copper (II) Salts
-
- KODAMA Eri
- Department of Applied Material and Life Science, College of Engineering, Kanto Gakuin University
-
- ONODERA Motomi
- Department of Applied Material and Life Science, College of Engineering, Kanto Gakuin University
-
- HARIMA Hideaki
- Department of Applied Material and Life Science, College of Engineering, Kanto Gakuin University
-
- UCHIDA Yoshikuni
- Department of Applied Material and Life Science, College of Engineering, Kanto Gakuin University
-
- MATSUI Kazunori
- Department of Applied Material and Life Science, College of Engineering, Kanto Gakuin University
Bibliographic Information
- Other Title
-
- Cu`2+´触媒を用いたポリアニリン‐シリカ複合ゲルの作製
- Cu²⁺触媒を用いたポリアニリン―シリカ複合ゲルの作製
- Cu ² ⁺ ショクバイ オ モチイタ ポリアニリン ― シリカ フクゴウ ゲル ノ サクセイ
Search this article
Abstract
Catalytic polymerization of aniline was carried out in sol-gel silicas doped with aniline and copper(II) salts as a catalyst in order to prepare polyaniline/silica hybrid gels. Aqueous solutions of aniline, sodium dodecyl sulfate, HCl, Cu(II) salts and tetraethoxysilane were mixed and stirred at room temperature. The obtained gels showed a deep green color during the drying process and had absorption peaks at ∼422 nm and ∼750 nm, thus indicating the formation of emeraldine salts type polyaniline in the sol-gel silicas. As for the formation of polyaniline, CuCl2 was twice as active as CuSO4 or Cu(NO3)2. It was confirmed that polymerization of polyaniline proceeds by utilizing copper(II) salts as a catalyst and oxygen as an oxidant in the sol-gel silica gels.
Journal
-
- Journal of the Japan Society of Colour Material
-
Journal of the Japan Society of Colour Material 84 (11), 369-372, 2011
Japan Society of Colour Material
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282679116131840
-
- NII Article ID
- 10030178180
-
- NII Book ID
- AN00354634
-
- COI
- 1:CAS:528:DC%2BC38XnsFSk
-
- ISSN
- 18832199
- 0010180X
-
- NDL BIB ID
- 023333562
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed