{312} Planar Faults in Slightly Vacuum-Reduced Rutile(TiO2)

  • Yagi Eiichi
    The Institute of Physical and Chemical Research
  • Hasiguti Ryukiti R.
    The Institute of Physical and Chemical Research Faculty of Engineering, University of Tokyo

書誌事項

タイトル別名
  • {312} Planar Faults in Slightly Vacuum-Reduced Rutile (TiO<SUB>2</SUB>)
  • 312 Planar Faults in Slightly Vacuum Re

この論文をさがす

説明

Electron microscopy on slightly vacuum-reduced rutile single crystals with a composition of about TiO1.996 revealed the presence of isolated planar faults with {312} fault plane. The displacement vector R of this fault was determined to be R\simeq1⁄2⟨10\bar1⟩. Discussion was made on the relation between such planar faults and defect centers observed in EPR experiments performed on the same specimens. The result on the displacement vector supports the interpretation of W-spectrum observed in the EPR experiments.