Nuclear Magnetic Resonance of Fe<SUP>57</SUP> in α-Fe<SUB>2</SUB>O<SUB>3</SUB>
-
- Matsuura Motohiro
- Department of Physics, Faculty of Science, Kyoto University
-
- Yasuoka Hiroshi
- Department of Physics, Faculty of Science, Kyoto University
-
- Hirai Akira
- Department of Physics, Faculty of Science, Kyoto University
-
- Hashi Tsuneo
- Department of Physics, Faculty of Science, Kyoto University
この論文をさがす
説明
Nuclear magnetic resonance (NMR) of Fe57 in α-Fe2O3 was studied by using both the steady-state method and the pulsed NMR method. The signal could be observed in the temperature range, where the sample shows the parasitic ferromagnetism. From the experimental results it was concluded that the NMR signal of this sample is due to the nuclei within the domain wall. The average enhancement factor of the applied rf magnetic field was measured to be about 25,000. The spin lattice relaxation time (T1) of Fe57 was distributed between 3 m sec and 100 msec at room temperature, depending upon the intensity of the exciting rf pulse. The values of T1 could be qualitatively explained by the relaxation mechanism due to the thermal domain wall fluctuation.
収録刊行物
-
- Ｊｏｕｒｎａｌ ｏｆ ｔｈｅ Ｐｈｙｓｉｃａｌ Ｓｏｃｉｅｔｙ ｏｆ Ｊａｐａｎ
-
Ｊｏｕｒｎａｌ ｏｆ ｔｈｅ Ｐｈｙｓｉｃａｌ Ｓｏｃｉｅｔｙ ｏｆ Ｊａｐａｎ 17 (7), 1147-1154, 1962
一般社団法人 日本物理学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679170063872
-
- NII論文ID
- 210000077185
- 130003732803
-
- BIBCODE
- 1962JPSJ...17.1147M
-
- COI
- 1:CAS:528:DyaF38Xks1Sntrg%3D
-
- ISSN
- 13474073
- 00319015
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可