Properties of Titanium Dioxide-polmyer Composite with Titanate Coupling Agents

DOI 2 Citations
  • YOSHIDA Keiichi
    Department of Fixed Prosthodontics, Nagasaki University School of Dentistry
  • MATSUMURA Hideo
    Department of Fixed Prosthodontics, Nagasaki University School of Dentistry
  • TANAKA Takuo
    Department of Fixed Prosthodontics, Nagasaki University School of Dentistry
  • ATSUTA Mitsuru
    Department of Fixed Prosthodontics, Nagasaki University School of Dentistry

Bibliographic Information

Other Title
  • チタネート系カップリング剤を応用した二酸化チタン-高分子複合体の諸性質

Search this article

Description

Titanium dioxide-polymethacrylate composites were prepared with triethyleneglycol dimethacrylate (TEGDMA), 1, 6-bis(methacryloxy-2-ethoxycarbonylamino)-2, 4, 4-trimethylhexane (UDMA) and rutile structure titanium dioxide. The coupling agents used were isopropyldimethacrylisostearoyl titanate (KR7), isopropyltri(dioctylphosphate)titanate (KR12) and 4-methacryloxyethyl trimellitate anhydride (4-META). Compressive and transverse strengths of composites were determined under various experimental conditions. Compressive strength of composite with KR7-treated titanium dioxide was higher than that with untreated titanium dioxide. Transverse strength of the composite with 4-META-treated titanium dioxide was higher than that with untreated titanium dioxide. Both compressive and transverse strengths increased when the titanium dioxide was treated with the mixture of KR7 and 4-META. Scanning electron microscopic observations of fractured composite surfaces showed titanium dioxide polymer interface failure with untreated specimens and polymer cohesive fracture with KR7+4-META-treated specimens. The results suggest that titanium dioxide treated with both KR7 and 4-META is useful as a pigment of the opaque material of fixed prosthodontic composite.