光酸素化処理した炭素繊維によるCFRCの高強度化
書誌事項
- タイトル別名
-
- Strengthening of CFRC with Photo-Oxygenated Carbon Fiber
この論文をさがす
説明
Surface modification of PAN based carbon fiber (CF) by photo-oxygenation was investigated to give high adhesion between CF and cement matrix to CF/cement composites (CFRC). Photooxygenation was carried out by radiating ultraviolet rays (120w, 184.9nm, 253.7nm) onto CF paper under ozone stream (normal pressure). CF surface was remarkably modified to hydrophobic by photo-oxygenation treatment. CFRC plates (thickness: 6mm) were prepared by laminating 12 sheets of CF paper preimpregnated with portland cement paste (W/C=40%), and cured in water (14 days). These CFRC plates prepared from CF paper pretreated by photo-oxygenation treatment, exhibited higher flexural strength compared with those from CF paper without photo-oxygenation treatment.<BR>The mechanical properties of CFRC prepared from photo-oxygenated CF paper were influenced by the temperature and time of treatment. The most effective condition of photo-oxygenation treatment on CF paper was the one at 150°C for 28min. The flexural strength (72MPa) of CFRC plate prepared with this photo-oxygenation on CF paper, was the largest of all.
収録刊行物
-
- 炭素
-
炭素 1994 (162), 71-77, 1994
炭素材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679203073920
-
- NII論文ID
- 130004121362
-
- ISSN
- 18845495
- 03715345
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可