Electrochemical Studies on Hot Corrosion of Ni–Cr–Al Alloys in Molten Na<SUB>2</SUB>SO<SUB>4</SUB>–NaCl
-
- Hara Motoi
- Department of Materials Engineering and Applied Chemistry, Mining College, Akita University
-
- Shinata Yutaka
- Department of Materials Engineering and Applied Chemistry, Mining College, Akita University
書誌事項
- タイトル別名
-
- Electrochemical Studies on Hot Corrosion of Ni–Cr–Al Alloys in Molten Na<SUB>2</SUB>SO<SUB>4</SUB>–NaCl
この論文をさがす
説明
The hot corrosion behavior of Ni-20%Cr-2%Al and −5%Al alloys in molten Na2SO4–NaCl was examined by the electrochemical measurement, the measurement of corrosion mass loss and the observation of corrosion morphology. The corrosion mass loss of both alloys was very large in mixed molten salts of Na2SO4 and NaCl. In the mixed molten salts, correspondingly, the anodic and cathodic reactions of the alloys in the vicinity of corrosion potential were very active. This suggests that this hot corrosion results from an electrochemical reaction. In addition, the electrochemical studies also indicated that the anodic and cathodic reactions for the hot corrosion seemed to be a preferential dissolution reaction of chromium from the alloys and a reduction reaction of CrO42− ions due to the dissolution reaction, respectively. This reaction model was supported by the observation results of a corrosion layer formed in the alloys. It was thought that such electrochemical corrosion was accelerated by a corrosion product.
収録刊行物
-
- Materials Transactions, JIM
-
Materials Transactions, JIM 33 (8), 758-768, 1992
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679222178432
-
- NII論文ID
- 130003556124
-
- COI
- 1:CAS:528:DyaK3sXhslekt70%3D
-
- ISSN
- 2432471X
- 09161821
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可