Non-Destructive Evaluation of Fatigue Damage in Type 316 Stainless Steel Using Positron Annihilation Lineshape Analysis
-
- Kawaguchi Yasuhiro
- Institute of Nuclear Technology, Institute of Nuclear Safety System, Inc.
-
- Nakamura Noriko
- Research Laboratory, Ishikawajima-Harima Heavy Industries Co., Ltd.
-
- Yusa Satoru
- Research Laboratory, Ishikawajima-Harima Heavy Industries Co., Ltd.
この論文をさがす
抄録
We applied positron annihilation lineshape analysis for non-destructive evaluation of fatigue stored in type 316 stainless steel, mainly used in primary water lines of pressurized water reactors (PWR). Using 68Ge as a positron source, an energy spread of annihilation gamma ray peaks from stainless steel specimens was measured. After preparing stress- and strain-controlled fatigue specimens, we investigated the relation between fatigue life and a non-destructive parameter of lineshape analysis defined as the S-parameter and compared the microstructure of the fatigue specimens with the S-parameter. As a result, there was good correlation between the S-parameter and fatigue life; the S-parameter increased with dislocation density monotonically. The relation between the S-parameter and fatigue life in stress-controlled fatigue differed from that in strain-controlled fatigue. The S-parameter increased faster in early stage of the latter than in the former. In stress-controlled fatigue, the change in the S-parameter did not depend on stress amplitude in the range of ratio to yield stress under 0.9. In the strain-controlled fatigue, the change in the S-parameter did not depend on strain amplitude in the range from 0.25 to 0.31%. However, when stress amplitude or strain amplitude became higher, the change in the S-parameter increased largely in the early stage of the fatigue life. We demonstrated systematic data to evaluate the fatigue damage in type 316 stainless steel.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (4), 727-734, 2002
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679222305792
-
- NII論文ID
- 10012322521
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD38XksF2rtro%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6263303
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可