Effects of Titanium Addition on the Microstructure and Mechanical Behavior of Iron Aluminide Fe3Al
-
- Zhu Su-Ming
- Japan Ultra-high Temperature Materials Research Institute
-
- Sakamoto Kazushi
- Japan Ultra-high Temperature Materials Research Institute
-
- Tamura Makoto
- Japan Ultra-high Temperature Materials Research Institute
-
- Iwasaki Kunihiko
- Japan Ultra-high Temperature Materials Research Institute
書誌事項
- タイトル別名
-
- Effects of Titanium Addition on the Microstructure and Mechanical Behavior of Iron Aluminide Fe<SUB><B>3</B></SUB>Al
この論文をさがす
説明
The microstructure, mechanical properties and deformation behavior of four Fe3Al-based alloys containing 0, 5, 10 or 15 at%Ti were investigated. With the addition of Ti, the coarse-grained microstructure of Fe3Al was refined and the degree of D03 ordering was decreased. Poor bending ductility and a change of fracture mode from cleavage to mixture of intergranular and cleavage were observed in Ti-added alloys. It was shown that the Ti addition decreased the room temperature yield strength, but increased the yield strength at elevated temperatures. Anomalous temperature dependence of yield strength was observed in all the alloys, and the peak strength was shifted to higher temperatures with increasing Ti content. The Ti addition was also revealed to decrease the strain rate sensitivity and activation energy for high temperature deformation. Finally, hot working conditions for the Ti-added Fe3Al alloys were proposed by taking the stress-strain response, strain rate sensitivity and deformation microstructure into account.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 42 (3), 484-490, 2001
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679222489472
-
- NII論文ID
- 130004451464
- 10006547691
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD3MXjtlSjtLo%3D
-
- ISSN
- 13475320
- 13459678
- http://id.crossref.org/issn/09161821
-
- NDL書誌ID
- 5729310
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可