Long-Range Order Parameter of Oriented L10-FePt Nanoparticles Determined by Electron Diffraction

DOI 機関リポジトリ 機関リポジトリ (HANDLE) 機関リポジトリ (HANDLE) Web Site ほか1件をすべて表示 一部だけ表示 被引用文献2件 参考文献49件 オープンアクセス
  • Sato Kazuhisa
    The Institute of Scientific and Industrial Research (ISIR-SANKEN), Osaka University
  • Hirotsu Yoshihiko
    The Institute of Scientific and Industrial Research (ISIR-SANKEN), Osaka University

書誌事項

タイトル別名
  • Long-Range Order Parameter of Oriented L1<SUB>0</SUB>-FePt Nanoparticles Determined by Electron Diffraction

この論文をさがす

説明

Two-dimensionally dispersed L10-FePt nanoparticles as small as 12 nm with orientation was fabricated by electron-beam evaporation and post-annealing at 873 K. After a prolonged annealing at 873 K for 86.4 ks, the increase of coercivity was almost saturated and coercivity reached 434 kAm−1 at 300 K, which is very small compared to recent reports on FePt nanoparticles with sizes larger than 20 nm. Long-range order parameter of the fabricated nanoparticles was determined by electron diffraction at 200 kV taking the multiple scattering into consideration. Obtained order parameter remained 0.55±0.02 for the nanoparticles with an axial ratio c⁄a of 0.961±0.003. The low degree of order is thought to be responsible for the small coercivity. Effect of Debye-Waller factor on the order parameter was discussed.