Fatigue Crack Growth in Laser Weldments of a Cold Rolled Steel

DOI Web Site 被引用文献2件 参考文献9件
  • Hwang Jiun-Ren
    Department of Mechanical Engineering, National Central University
  • Doong Ji-Liang
    Department of Mechanical Engineering, National Central University
  • Chen Chee-Chang
    Department of Mechanical Engineering, National Central University

説明

This paper describes the effect of laser welding process on the fatigue crack propagation in SPCC-CQ1 cold rolled steel. The influences of weld speed and gap width of butt joint on fatigue crack growth rate are considered. Strength of the weld joints is evaluated by a tensile test, while fatigue properties are investigated by fatigue crack propagation test based on linear elastic fracture mechanics. From the results, the added wire filler material had positive effect on the fatigue properties. Increasing welding speed or gap width will improve the resistance to fatigue crack growth because of fast cooling rate and refined equiaxed microstructure in fusion zone. Also, the fatigue crack growth rate of fusion zone and heat affected zone are lower than that of base metal. Transgranular fracture is the typical fracture mechanism and many secondary cracks appear in the fusion zone.

収録刊行物

被引用文献 (2)*注記

もっと見る

参考文献 (9)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ