Cooling Rate Evaluation for Bulk Amorphous Alloys from Eutectic Microstructures in Casting Processes
-
- Srivastava Raghvendra Mohan
- Department of Metallurgy & Materials Engineering, Indian Institute of Technology, Kharagpur
-
- Eckert Jürgen
- IFW Dresden, Institut für Metallische Werkstoffe
-
- Löser Wolfgang
- IFW Dresden, Institut für Metallische Werkstoffe
-
- Dhindaw Brij Kumar
- Department of Metallurgy & Materials Engineering, Indian Institute of Technology, Kharagpur
-
- Schultz Ludwig
- IFW Dresden, Institut für Metallische Werkstoffe
この論文をさがす
説明
The structural features of metallic glasses depend on the cooling rate of the melt. The cooling rates for casting processes which are typically employed for preparation of bulk metallic glasses are suggested from microstructures of an eutectic Al–33 mass%Cu model alloy. The interlamellar spacing λ of eutectic Al–CuAl2 rod-shaped specimens of 50 mm in length and 2 to 5 mm in diameter has been determined by optical microscopy and scanning electron microscopy. From the measured interlamellar spacings ranging from λ=0.18 to 0.5 \\micron, the solidification front velocities and the cooling rates at different positions in the as-cast samples are derived. The decisive effect of the diameter of cast rods is confirmed. For a centrifugal casting technique, the maximum cooling rate decreases from 730 to 95 K/s when the diameter increases from 2 to 5 mm. Moreover, it is revealed that the local cooling rates decrease significantly from the bottom towards the top of the rods. From the estimated cooling rates at a fixed rod diameter the centrifugal casting technique is assessed as superior to other methods applied, namely copper-mould casting and suction casting. The estimated cooling rates are compared with literature data for glass-forming alloys.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 43 (7), 1670-1675, 2002
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679223527296
-
- NII論文ID
- 130004451881
- 10012325492
- 30018849787
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD38Xmt1equ7c%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6241175
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可