Kinetics of Austenite to Ferrite Transformation in 3 mass% Mn Low Carbon Steels
-
- Enomoto M.
- Department of Materials Science, Ibaraki University
-
- Sonoyama T.
- Department of Materials Science, Ibaraki University
-
- Yada H.
- Department of Mechanical Engineering, Shizuoka Institute of Science and Technology
書誌事項
- タイトル別名
-
- Kinetics of Austenite to Ferrite Transf
- 公開日
- 1998
- DOI
-
- 10.2320/matertrans1989.39.189
- 公開者
- 社団法人 日本金属学会
この論文をさがす
説明
The kinetics of isothermal austenite to ferrite transformation in low carbon steels was studied theoretically. The transformation rates were calculated in steels containing 3 mass% Mn assuming various modes of transformation, i.e. massive, paraequilibrium and ternary (Fe–C–Mn) local equilibrium. A crude comparison was made with experimentally observed microstructures. The transformation is likely to occur accompanying carbon diffusion not only in the (α+γ) two phase field, but also in the α single phase field. In contrast, diffusion of Mn is unlikely to occur, or may not play a major role in the transformation.
収録刊行物
-
- Materials Transactions, JIM
-
Materials Transactions, JIM 39 (1), 189-195, 1998
社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679223545600
-
- NII論文ID
- 130003422514
- 40005337903
-
- NII書誌ID
- AA10699969
-
- COI
- 1:CAS:528:DyaK1cXitFeru7Y%3D
-
- ISSN
- 2432471X
- 09161821
-
- NDL書誌ID
- 4406276
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可