Mechanical Properties of Mg-Y-Zn Alloy Processed by Equal-Channel-Angular Extrusion
-
- Watanabe Hiroyuki
- Osaka Municipal Technical Research Institute
-
- Mukai Toshiji
- Osaka Municipal Technical Research Institute
-
- Kamado Shigeharu
- Department of Mechanical Engineering, Nagaoka University of Technology
-
- Kojima Yo
- Department of Mechanical Engineering, Nagaoka University of Technology
-
- Higashi Kenji
- Department of Metallurgy and Materials Science, Osaka Prefecture University
この論文をさがす
抄録
Fine-grained WZ73 magnesium alloy with the grain size of 1.6 μm was produced by Equal-Channel-Angular Extrusion. The material exhibited tensile yield strength of 293 MPa, tensile strength of 350 MPa and relatively large elongation of 18% at room temperature. The yield strength was almost unchanged up to 473 K. In addition, large superplastic elongation of over 300% was obtained at a temperature of 673 K.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 44 (4), 463-467, 2003
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679223932672
-
- NII論文ID
- 130004452074
- 30018849768
- 10011910382
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD3sXkslClsr0%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 6513430
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可