Bulk Glassy Fe<SUB>78-x</SUB>Co<SUB>x</SUB>Ga<SUB>2</SUB>P<SUB>12</SUB>C<SUB>4</SUB>B<SUB>4</SUB> Alloys with High Saturation Magnetization and Good Soft Magnetic Properties

DOI Web Site Web Site 3 Citations 31 References

Bibliographic Information

Other Title
  • Bulk Glassy Fe78-xCoxGa2P12C4B4 Alloys with High Saturation Magnetization and Good Soft Magnetic Properties

Search this article

Abstract

The effect of Co on the magnetic properties and glass-forming ability for the Fe78−xCoxGa2P12C4B4 glassy alloys was investigated. The addition of 4 to 8 at%Co was found to be effective for the extension of the supercooled liquid region (ΔTx) defined by the difference between the glass transition temperature (Tg) and crystallization temperature (Tx). The ΔTx value is 26 K for the Fe78Ga2P12C4B4 alloy and increases to 37 K for the 4 at%Co alloy. Besides, the addition of a small amount of Co was also found to be effective for increasing the saturation magnetization (Is) and decreasing the coercive force (Hc). These glassy ribbon alloys exhibit good soft magnetic properties of 1.36 to 1.43 T for saturation magnetization and 1.5 to 1.8 A/m for coercive force. The largest saturation magnetization (Is) is 1.43 T for Fe74Co4Ga2P12C4B4 alloy. Based on its large ΔTx, we tried to prepare bulk glassy Fe74Co4Ga2P12C4B4 rods in a cylindrical form with different diameters. The glassy single phase was obtained in the diameter of 0.5 and 1.0 mm. These bulk glassy alloys also exhibit high saturation magnetization of about 1.42 T.

Journal

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 42 (6), 1052-1055, 2001

    The Japan Institute of Metals and Materials

Citations (3)*help

See more

References(31)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top