Enhancement of the Photoluminescence from Porous Silicon by Anodic Polarization
-
- Arigane Tsuyoshi
- Department of Materials Science, Graduate School of Engineering, Tohoku University
-
- Watanabe Noriyuki
- Department of Materials Science, Graduate School of Engineering, Tohoku University
-
- Wadayama Toshimasa
- Department of Materials Science, Graduate School of Engineering, Tohoku University
-
- Hatta Aritada
- Department of Materials Science, Graduate School of Engineering, Tohoku University
この論文をさがす
抄録
Photoluminescence (PL) spectral change in porous silicon (PS) was investigated during post-anodization in 0.1 kmol/m3 KCl and 0.1 kmol/m3 HClO4 aqueous solutions. The PL intensities of the PS immersed in both solutions were enhanced with an increase of the current density of anodization. The PL enhancement occurred without either change in the size of the silicon nano-crystallites in the PS or chemical properties of the PS. When the PS was made free of anodization, the PL reverted to the initial state. However, the rate at which the PL was restored to the initial state was higher in the KCl solution than in the HClO4 solution. These results suggest an involvement of the anionic species in the PL enhancement.
収録刊行物
-
- Materials Transactions, JIM
-
Materials Transactions, JIM 40 (3), 182-185, 1999
社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679225311744
-
- NII論文ID
- 130003422591
- 10003805687
-
- NII書誌ID
- AA10699969
-
- COI
- 1:CAS:528:DyaK1MXjsFWqurg%3D
-
- ISSN
- 2432471X
- 09161821
-
- NDL書誌ID
- 4689623
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可