Controlling Oxygen Content by Varying Oxygen Partial Pressure in Chromium Oxynitride Thin Films Prepared by Pulsed Laser Deposition
-
- Suzuki Kazuma
- Extreme Energy-Density Research Institute, Nagaoka University of Technology
-
- Endo Toshiyuki
- Extreme Energy-Density Research Institute, Nagaoka University of Technology
-
- Fukushima Teruhisa
- Extreme Energy-Density Research Institute, Nagaoka University of Technology
-
- Sato Aoi
- Extreme Energy-Density Research Institute, Nagaoka University of Technology
-
- Suzuki Tsuneo
- Extreme Energy-Density Research Institute, Nagaoka University of Technology
-
- Nakayama Tadachika
- Extreme Energy-Density Research Institute, Nagaoka University of Technology
-
- Suematsu Hisayuki
- Extreme Energy-Density Research Institute, Nagaoka University of Technology
-
- Niihara Koichi
- Extreme Energy-Density Research Institute, Nagaoka University of Technology
この論文をさがす
抄録
Chromium oxynitride Cr(N,O) thin films were prepared by pulsed laser deposition in a highly reactive atmosphere, which consisted of pure oxygen gas and nitrogen plasma from a radio-frequency radical source. In order to control the oxygen content in the thin films, oxygen partial pressure (PO<sub>2</sub>) in the chamber was varied from 5 to 10 × 10−5 Pa under a fixed total pressure of 1.5 × 10−2 Pa. The thin films were then characterized by X-ray diffraction, infrared spectroscopy, electron energy loss spectroscopy and nano-indentation testing. It was found that the oxygen content of the thin films changed from 0 to 62 mol% with increasing PO<sub>2</sub>. The thin films with only the NaCl-type (B1) Cr(N,O) phase were prepared under PO<sub>2</sub> < 7.5 × 10−5 Pa. The chromium content of the B1 phase decreased from 47 mol%, which was close to the stoichiometric composition of CrN, to 40 mol% when the oxygen content was increased. The hardness increased up to 32 GPa with increasing PO<sub>2</sub> up to 7.5 × 10−5 Pa.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 54 (7), 1140-1144, 2013
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679225598208
-
- NII論文ID
- 10031183658
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BC3sXhsVGjtrbL
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 024647548
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可