Effect of Silicate Ions on Conversion of Ferric Hydroxide to β-FeOOH and α-Fe2O3
-
- Kwon Sang-Koo
- Institute of Multidisciplinary Research for Advanced Materials, Tohoku University
-
- Kimijima Ken’ichi
- Institute of Multidisciplinary Research for Advanced Materials, Tohoku University
-
- Kanie Kiyoshi
- Institute of Multidisciplinary Research for Advanced Materials, Tohoku University
-
- Muramatsu Atsushi
- Institute of Multidisciplinary Research for Advanced Materials, Tohoku University
-
- Suzuki Shigeru
- Institute of Multidisciplinary Research for Advanced Materials, Tohoku University
-
- Matsubara Eiichiro
- Institute for Materials Research, Tohoku University
-
- Waseda Yoshio
- Institute of Multidisciplinary Research for Advanced Materials, Tohoku University
書誌事項
- タイトル別名
-
- Effect of Silicate Ions on Conversion of Ferric Hydroxide to β-FeOOH and α-Fe<SUB>2</SUB>O<SUB>3</SUB>
- Effect of Silicate Ions on Conversion of Ferric Hydroxide to ベータ FeOOH and アルファ Fe2O3
- Effect of Silicate Ions on Conversion of Ferric Hydroxide to β-FeOOH and α-Fe<SUB>2</SUB>O<SUB>3</SUB>
この論文をさがす
抄録
Ferric hydroxide (Fe(OH)3) gel, prepared from FeCl3 and NaOH solutions, was aged at 100°C in the presence and absence of silicate ions to examine the effect of silicate ions on the conversion process of condensed Fe(OH)3 gel to iron oxides. The aged suspensions containing colloidal particles in each stage were separated into solid particles and supernatant solutions by centrifugation. X-ray diffraction measurements and transmission electron microscopic observations of the solid particles revealed that β-FeOOH was formed from the Fe(OH)3 gel and subsequently converted into α-Fe2O3, and the addition of silicate ions in the Fe(OH)3 gel decreased the conversion rate to β-FeOOH and α-Fe2O3 particles. IR measurements of the solid particles and inductively coupled plasma analyses of the supernatant solutions showed that the adsorption of silicate ions on specific plane of the solid particles was decisive factor for the suppression of the conversion process.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 46 (2), 155-158, 2005
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679225691520
-
- NII論文ID
- 10014416956
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BD2MXjtFWlt7k%3D
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 7256645
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可