Structural Characterization of Stress-Induced Martensitic Transformation in a Polycrystalline Austenitic Fe-Mn-Si-Cr Alloy

DOI Web Site Web Site 被引用文献5件 参考文献28件 オープンアクセス

書誌事項

公開日
2008
DOI
  • 10.2320/matertrans.mra2008034
公開者
公益社団法人 日本金属学会

この論文をさがす

説明

Stress-induced martensitic transformation in Fe-Mn-Si alloys is characterized by the transformation of the fcc matrix to the hcp phase, which is generally reversible. In this study, Debye rings obtained by monochromated X-ray diffraction using synchrotron radiation were used for analyzing the structural change of the fcc matrix to the hcp phase in a polycrystalline austenitic Fe-Mn-Si-Cr alloy that was deformed by the tensile test at room temperature. Structural changes resulting from the reverse transformation due to heating were also studied. The results showed that the occurrence of the stress-induced martensitic transformation was not uniform, but depended on the relationship between the orientation of polycrystalline grains and the tensile direction. The transformation appears to preferentially occur in grains with large Schmid factors for the shear of [\\bar211](111) in the fcc matrix, and the formation of hcp phases also depends on the orientation of grains. The reverse transformation due to heating does not necessarily occur in the crystallographically reversible route. This indicates that irreversible deformation induced by dislocations during the tensile test restricts the reversible transformation of the alloy.

収録刊行物

被引用文献 (5)*注記

もっと見る

参考文献 (28)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ