Aluminide coatings fabricated on nickel by aluminium electrodeposition from DMSO2-based electrolyte and subsequent annealing
-
- Shiomi Suguru
- Graduate School of Energy Science, Kyoto University
-
- Miyake Masao
- Graduate School of Energy Science, Kyoto University
-
- Hirato Tetsuji
- Graduate School of Energy Science, Kyoto University
-
- Sato Akihiro
- Corporate Research & Development, IHI Corporation
書誌事項
- タイトル別名
-
- Aluminide Coatings Fabricated on Nickel by Aluminium Electrodeposition from DMSO<SUB>2</SUB>-Based Electrolyte and Subsequent Annealing
この論文をさがす
説明
A new cost-effective process to fabricate aluminide coatings was developed. Coating layers consisting of nickel aluminides could be formed by electrodeposition of Al layers from a dimethylsulfone-AlCl3 electrolyte on Ni substrates and subsequent annealing in air or vacuum at temperatures of 700–1150°C. Analysis of the intermetallic layers by XRD, SEM and EDX indicated the formation of Al3Ni and Al3Ni2 at 700°C, AlNi at 900°C and 1000°C, and AlNi and AlNi3 at 1150°C. The Annealing atmosphere did not affect the resulting intermetallic products.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 52 (6), 1216-1221, 2011
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679225841536
-
- NII論文ID
- 10028252780
-
- NII書誌ID
- AA1151294X
-
- COI
- 1:CAS:528:DC%2BC3MXhtVOqs7vM
-
- ISSN
- 13475320
- 13459678
-
- HANDLE
- 2433/237642
-
- NDL書誌ID
- 11106814
-
- 本文言語コード
- en
-
- 資料種別
- journal article
-
- データソース種別
-
- JaLC
- IRDB
- NDLサーチ
- Crossref
- CiNii Articles
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可