Novel Hydrides in Li-TM Systems Synthesized by High Pressure Method (TM=Ti, Zr, Hf)
-
- Kataoka Riki
- Department of Materials Science, Graduate School of Engineering, Tohoku University
-
- Sato Toyoto
- WPI Advanced Institute for Materials Research, Tohoku University
-
- Kuriiwa Takahiro
- Department of Materials Science, Graduate School of Engineering, Tohoku University
-
- Kamegawa Atsunori
- Department of Materials Science, Graduate School of Engineering, Tohoku University
-
- Okada Masuo
- Department of Materials Science, Graduate School of Engineering, Tohoku University
この論文をさがす
抄録
New Li-based hydrides have been prepared under GPa-order by using a cubic-anvil-type apparatus. Novel compounds in Li-Zr and Li-Hf systems were obtained at 973 K under 5 GPa. For Li-Zr system, a novel compound has a primitive cubic structure with a=0.42188(3) nm. The compound was thermally stable up to 723 K under Ar flow. For Li-Hf system, two novel compounds were successfully synthesized. Crystal structures of these compounds were found to be a primitive cubic (a=0.4209(2) nm) and a body centered cubic (a=1.08369(4) nm). A structural model of the new compounds with the body-centered cubic structure was found to be an Ag8Ca3-type structure. The novel compound with a primitive cubic structure was thermally stable up to 723 K, but the compound with the body centered cubic structure was decomposed at 600 K with an endothermic reaction.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 52 (1), 49-53, 2011
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679226252160
-
- NII論文ID
- 10027672195
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 10926905
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可