Dielectric Property of Polycrystalline ZrO<SUB>2</SUB> Substituted BaTi<SUB>2</SUB>O<SUB>5</SUB> Prepared by Arc-Melting
-
- Yue XinYan
- Institute for Materials Research, Tohoku University
-
- Tu Rong
- Institute for Materials Research, Tohoku University
-
- Goto Takashi
- Institute for Materials Research, Tohoku University
Bibliographic Information
- Other Title
-
- Dielectric property of polycrystalline ZrO2 substituted BaTi2O5 prepared by arc-melting
Search this article
Abstract
ZrO2 substituted polycrystalline BaTi2O5, Ba(Ti1−yZry)2O5, (BT2Z), was prepared by arc-melting and the dielectric property was investigated by AC impedance spectroscopy. The length of a-axis increased from 1.6895 to 1.6952 nm and that of c-axis increased from 0.9411 to 0.9436 nm with increasing y up to 0.06. The b-axis was almost independent of ZrO2 content. The solubility limit of ZrO2 (y) in BT2Z can be 0.06. BT2Z had a strong b-axis orientation at y<0.06. The permittivity of BT2Z at y=0.005 showed the highest peak of 3050 at 725 K and the peak temperature decreased from 750 to 465 K with increasing y from 0 to 0.064. A relaxor-like frequency dependence of permittivity was observed at y>0.06.
Journal
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 49 (1), 120-124, 2008
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390282679226266368
-
- NII Article ID
- 10020088756
- 130004453748
-
- NII Book ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- HANDLE
- 10097/52188
-
- NDL BIB ID
- 9319875
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed