Structural Analysis of Polycrystalline BiFeO3 Films by Transmission Electron Microscopy
-
- Naganuma Hiroshi
- Department of Applied Physics, Faculty of Science, Tokyo University of Science
-
- Kovacs Andras
- The Institute of Scientific and Industrial Research, Osaka University
-
- Hirata Akihiko
- The Institute of Scientific and Industrial Research, Osaka University
-
- Hirotsu Yoshihiko
- The Institute of Scientific and Industrial Research, Osaka University
-
- Okamura Soichiro
- Department of Applied Physics, Faculty of Science, Tokyo University of Science
書誌事項
- タイトル別名
-
- Structural Analysis of Polycrystalline BiFeO<SUB>3</SUB> Films by Transmission Electron Microscopy
この論文をさがす
抄録
A multiferroic polycrystalline BiFeO3 film has been fabricated by a chemical solution deposition followed by the post deposition annealing at 823 K in air. The nanostructure of the BiFeO3 film was characterized by transmission electron microscopy (TEM). The nano-beam electron diffraction and the fast Fourier transform pattern image from the high resolution TEM image were compared with the electron diffraction patterns of the multislice simulation, and it was revealed that the BiFeO3 has R3c rhombohedral structure. Formation of any additional phase or phases was not found in the sample. The BiFeO3 film shows the small saturation magnetization of 5.2 emu/cm3 without spontaneous magnetization at room temperature, which behavior is typical for the weak ferromagnetic materials. The ferroelectric hysteresis loop of the BiFeO3 film was measured at low temperature in order to reduce the leakage current. The remanent polarization and the electric coercive field at 90 K were 52 μC/cm2 and 0.51 MV/cm at an applied electric field of 1.4 MV/cm, respectively. The structure-magnetic properties relationship is also discussed.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 48 (9), 2370-2373, 2007
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679226278656
-
- NII論文ID
- 10019853478
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- HANDLE
- 10097/52013
-
- NDL書誌ID
- 8884979
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可