Cyclic hydrogenation and dehydrogenation property of LiNH2 impregnated into Ni foam
-
- Menjo Masaharu
- Institute for Materials Research, Tohoku University
-
- Hyodo Yoshihiro
- Institute for Materials Research, Tohoku University
-
- Moriyama Satoko
- Institute for Materials Research, Tohoku University
-
- Li Hai-Wen
- Institute for Materials Research, Tohoku University
-
- Matsuo Motoaki
- Institute for Materials Research, Tohoku University
-
- Semboshi Satoshi
- Institute for Materials Research, Tohoku University
-
- Orimo Shin-ichi
- Institute for Materials Research, Tohoku University
書誌事項
- タイトル別名
-
- Cyclic Hydrogenation and Dehydrogenation Property of LiNH<SUB>2</SUB> Impregnated into Ni Foam
この論文をさがす
抄録
Cyclic hydrogenation and dehydrogenation property of LiNH2 impregnated into the Ni foam was experimentally investigated, comparing with that of conventional LiNH2 powder. The amount of dehydrogenation from the impregnated sample after activating was 4.3 mass% (without the weight of the Ni foam), and remained 3.3 mass% after the 49th cycle of hydrogenation and dehydrogenation, while the amount from the powder sample drastically decreased down to 0.5 mass% until only the 11th cycle. The main origin of the superior cyclic property of the impregnated sample was attributed to the suppression of sintering, mainly due to release of the exothermic heat during the hydrogenation supported by the frames of the Ni foam.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 52 (4), 623-626, 2011
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679226315264
-
- NII論文ID
- 10028174948
- 130004454683
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 11058204
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可