Cooperative catalysis on the dehydrogenation of NdCl3 doped LiBH4-MgH2 composites
-
- Wang H.
- School of Materials Science and Engineering, South China of University of Technology
-
- Zhang H. L.
- School of Materials Science and Engineering, South China of University of Technology
-
- Luo C.
- School of Materials Science and Engineering, South China of University of Technology
-
- Sun T.
- School of Materials Science and Engineering, South China of University of Technology
-
- Zhu M.
- School of Materials Science and Engineering, South China of University of Technology
書誌事項
- タイトル別名
-
- Cooperative Catalysis on the Dehydrogenation of NdCl<SUB>3</SUB> Doped LiBH<SUB>4</SUB>-MgH<SUB>2</SUB> Composites
この論文をさがす
抄録
To improve the dehydrogenation properties of LiBH4, the MgH2 and NdCl3 were added with different modes by ball-milling, and their influences on the decomposition of LiBH4 were investigated by performing X-ray diffraction (XRD) analysis and dehydriding kinetic measurements. The results show that adding either NdCl3 or MgH2 alone could not promote the decomposition of LiBH4. But for the NdCl3 doped LiBH4-MgH2 composites, not only the decomposition of MgH2 is accelerated, but also the dehydrogenation rate and capacity of LiBH4 are greatly enhanced. The kinetic improvement is attributed to a cooperative catalytic role arising from dual addition of MgH2 and NdCl3. The NdH2 phase, resulting from reaction between MgH2 and NdCl3, might be responsible for the enhanced dehydrogenation of LiBH4.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 52 (4), 647-650, 2011
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679226318464
-
- NII論文ID
- 10028175082
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 11058241
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可