Formation and Thermal Stability of Ni-Based Bulk Metallic Glasses in Ni-Zr-Nb-Al System
-
- Qiang J. B.
- Institute for Materials Research (IMR), Tohoku University
-
- Zhang W.
- Institute for Materials Research (IMR), Tohoku University
-
- Inoue A.
- Institute for Materials Research (IMR), Tohoku University
この論文をさがす
抄録
An Al element was selected as an alloying metal to improve the glass-forming ability (GFA) of Ni-Zr-Nb alloys. The thermal stability and glass-forming ability of Ni-Zr-Nb-Al alloys were investigated. It was found that the partial substitution of Nb by Al led to significant shift of the onset crystallization temperature Tx and the liquidus temperature Tl, while the glass transition temperature Tg was less composition sensitive. The supercooled liquid region, ΔTx (=Tx−Tg), the reduced glass transition temperature (Tg⁄Tl) and γ=Tx⁄(Tg+Tl) increased with increasing Al content up to 5 at%. The best GFA was found at Ni60Zr20Nb15Al5 with a critical diameter of 3 mm. The characteristic parameters are: ΔTx=54 K, Tg⁄Tl=0.615 and γ=0.405. The maximum values of ΔTx and Tg⁄Tl were 72 K and 0.617, respectively, at Ni60Zr25Nb10Al5. The compression tests showed that the Ni60Zr20Nb15Al5 BMG possessed high fracture strength of 2900 MPa, Young’s modul of 152 GPa, and plastic elongation of 2.5% at room temperature.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 48 (9), 2385-2389, 2007
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679226763648
-
- NII論文ID
- 10019853556
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 8885140
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可