Superconducting properties of MgB2 particle impregnated with Mg-based alloys

DOI Web Site Web Site 被引用文献2件 参考文献44件

書誌事項

タイトル別名
  • Superconducting Properties of MgB<SUB>2</SUB> Particle Impregnated with Mg-Based Alloys

この論文をさがす

説明

The three-dimensional penetration method combined with semi-solid casting (SS-3DPC) was utilized to prepare magnesium diboride (MgB2) powder composite materials with various host materials of Mg, Mg-3%Al, Mg-3%Al-1%Zn, Mg-9%Al, and Mg-9%Al-1%Zn. X-ray diffraction measurements indicated predominant peak patterns of MgB2 and a host alloy, implying that the host material tightly bonded MgB2 grains without melting the MgB2 powder. This was confirmed by SEM images. Measured electrical resistivity and magnetization versus temperature showed clear signals of superconducting transition temperature of 27∼38 K for all the samples cut out from the billets. Magnetic hysteresis loop observed at 5 K enabled us to estimate a critical current density (Jc) based on the extended Bean model. Additions of aluminum and zinc elements to magnesium host-matrix were found to enhance Jc and increase residual resistivity (ρ0) suggesting that aluminum and zinc have an effect on pinning magnetic flux flow for Jc enhancement, and scattering conduction electrons for increase of ρ0.

収録刊行物

被引用文献 (2)*注記

もっと見る

参考文献 (44)*注記

もっと見る

関連プロジェクト

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ