Four-Dimensional Annihilation Behaviors of Micro Pores during Surface Cold Working

DOI Web Site Web Site 被引用文献9件 参考文献39件

この論文をさがす

抄録

The annihilation behavior of micro pores in an aluminum alloy casting during surface cold working was continuously observed using the synchrotron radiation microtomography. To analyze micro pore annihilation behavior, the displacement of artificially dispersed particles was measured and thereby local strain distributions were mapped in high-density. A peening treatment annihilated most of the micro pores with a diameter of over 10 μm in the upper part of the specimen that could initiate fatigue cracks. The annihilation behavior of the micro pores could be understood as a function of effective strain locally accumulated around them, and not as a function of local hydrostatic strain. The effective strain varied significantly, with some large pores remaining where local effective plastic strain was relatively low. The complete annihilation of large pores in the surface layer suggests that the application of sufficiently long surface cold working is effective in improving the high-cycle fatigue properties.

収録刊行物

被引用文献 (9)*注記

もっと見る

参考文献 (39)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ