Comparison of Microstructure and Oxidation Behavior of CoNiCrAlY Bond Coatings Prepared by Different Thermal Spray Processes

この論文をさがす

抄録

To protect various gas turbine components against high temperature in the hot sections of power generation plants and aircraft engines, thermal barrier coatings (TBCs) have been developed and widely used. Conventional TBCs consist of a MCrAlY bond coating for oxidation resistance and a ceramic top coating for thermal insulation. High quality coatings of MCrAlYs have been produced mostly by low pressure plasma spraying but other more economical processes are also used depending on the operating conditions of the component to be coated. In this study, CoNiCrAlY powders were deposited on Inconel 718 substrate with 3 types spraying system, i.e., low pressure plasma spraying, high velocity oxy-fuel spraying, and atmosphere plasma spraying. The specimens without top ceramic coating were isothermally tested for up to 100 hrs in air at 1373 K and mass gain of the coatings was measured. Microstructure of the coating cross sections and the surface oxides were observed with SEM. Moreover, phase changes during the oxidation test were investigated with calculated phase diagrams for the CoNiCrAlY alloy.

収録刊行物

被引用文献 (7)*注記

もっと見る

参考文献 (38)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ