Detection of micro-damage evolution of air plasma-sprayed Y_2O_3-Zro_2 thermal barrier coating through TGO stress measurement
-
- Tanaka M.
- Center for Collaborative Research, The University of Tokyo
-
- Hasegawa M.
- Research Center for Advanced Science and Technology, The University of Tokyo
-
- Kagawa Y.
- Center for Collaborative Research, The University of Tokyo Research Center for Advanced Science and Technology, The University of Tokyo
書誌事項
- タイトル別名
-
- Detection of Micro-Damage Evolution of Air Plasma-Sprayed Y<SUB>2</SUB>O<SUB>3</SUB>-ZrO<SUB>2</SUB> Thermal Barrier Coating through TGO Stress Measurement
この論文をさがす
抄録
The micro damage evolution behavior in air plasma-sprayed 8 mass% Y2O3 stabilized ZrO2 thermal barrier coating (APS-TBC) after isothermal heat exposure at 1150°C up to 200 h was observed. Residual stress of thermally-grown-oxide (TGO) layer was measured through the TBC layer using Cr3+ luminescence spectroscopy and the measured stress levels were compared with micro damage evolution behavior stored in the TBC system. With heat exposure time of longer than 10 h, microfracture behaviors were noted in the TBC layer. In-plane residual stress of the TGO layer increased for up to 50 h of heat exposure time, and thereafter, diminished with further increase. These behaviors are strongly correlated with the thickness and the residual stress of the TGO layer. This decrease in the TGO stress well contrasts with the evolution of the micro fracture behavior, which is also related to the thickness and undulation of the formed TGO layer. The change of TGO stress, σtgo, depending on the average thickness of the TGO layer, \\barhtgo, i.e., dσtgo⁄d\\barhtgo is a useful indicator of the damage evolution in TGO: dσtgo⁄d\\barhtgo>0: slight damage stage, dσtgo⁄d\\barhtgo<0: micro fracture evolution stage. The result suggests that Cr3+ luminescence spectroscopy is a good indicator for micro damage evolution in the TBC layer and is a useful tool for nondestructive evaluation (NDE) of APS-TBC systems.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 47 (10), 2512-2517, 2006
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679227113088
-
- NII論文ID
- 10018310256
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 8092083
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可