Characteristics of Fe-Cr-Al Alloy Nanopowders Prepared by Electrical Wire Explosion Process under Liquid Media
-
- Yun Jung-Yeul
- Functional Materials Division, Korea Institute of Materials Science
-
- Lee Hye-Moon
- Functional Materials Division, Korea Institute of Materials Science
-
- Choi Si-Young
- Functional Materials Division, Korea Institute of Materials Science
-
- Yang SangSun
- Functional Materials Division, Korea Institute of Materials Science
-
- Lee Dong-Won
- Functional Materials Division, Korea Institute of Materials Science
-
- Kim Young-Jin
- Functional Materials Division, Korea Institute of Materials Science
-
- Kim Byoung-Kee
- School of Materials Science and Engineering, University of Ulsan
この論文をさがす
抄録
Fe-Cr-Al alloy nanopowders were successfully prepared by electrical wire explosion method in ethyl alcohol media. The formation of Fe-Cr-Al alloy nanopowder was monitored by X-ray diffraction. The alloy powders have spherical shape and nanometer size. The alloy powders prepared by the electrical wire explosion method have main crystal structures of bcc Fe-Cr alloy. The geometric mean diameter and geometric standard deviation of an alloy powder formed from a wire with diameter of 0.1 mm were 10.2 nm and 1.62, respectively. However, the geometric mean diameter and geometric standard deviation of an alloy powder formed from a wire with diameter of 0.2 mm were 15.4 nm and 1.66, respectively. These values indicate that the particle size of the alloy powders prepared by the EWE method was increased with wire diameter. Fe, Cr, and Al components are uniformly dispersed inside the powder.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 52 (2), 250-253, 2011
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390282679227231872
-
- NII論文ID
- 10027837851
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 10958998
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可