The effect of jetting temperature on the fabrication of rapidly solidified Fe-Si-B systems alloys using roller melt spinning
-
- Nakagawa Keiyu
- Faculty of Engineering, Okayama University of Science
-
- Kanadani Teruto
- Faculty of Engineering, Okayama University of Science
-
- Mori Yasuyuki
- Faculty of Engineering, Okayama University of Science
-
- Ishii Yuto
- Faculty of Engineering, Okayama University of Science
書誌事項
- タイトル別名
-
- The Effect of Jetting Temperature on the Fabrication of Rapidly Solidified Fe-Si-B Systems Alloys Using Single-Roller Melt Spinning
この論文をさがす
抄録
Fe-Si-B systems amorphous alloys were rapidly solidified from the melt by the single roller method. In this process the alloys were melted in a crucible and the molten alloy is jetted through a small orifice by gas pressure or gravity. The effects of the jetting temperature of the melting alloy on the ribbon thickness of rapidly solidified Fe75Si10B15 and Fe79.5Si8.5B12 alloys were examined. The rapidly solidified Fe75Si10B15 and Fe79.5Si8.5B12 alloy ribbons’ mean thickness decreased continuously with the increased jetting temperature. However, the temperature dependence of the ribbon thickness in the Fe79.5Si8.5B12 alloy was greater than that of the Fe75Si10B15 alloy.<BR>The results demonstrate that the viscosity of liquid Fe-Si-B systems alloys influences the ribbon thickness. Moreover, when the contact conditions between the rotating roll comes and puddle are good, the ribbon thickness decreases.
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 52 (2), 196-200, 2011
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390282679227259648
-
- NII論文ID
- 10027837622
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 10958921
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可