The Microstructure and Wear Properties of Laser-Clad WC-Cr<SUB>3</SUB>C<SUB>2</SUB> Cermet Coating on Steel Substrate

DOI Web Site Web Site 1 Citations 24 References
  • Wu Qianlin
    Institute of Marine Materials Science and Engineering, Shanghai Maritime University
  • Li Wenge
    College of Materials Engineering, Shanghai University of Engineering Science

Bibliographic Information

Other Title
  • The microstructure and wear properties of laser-clad WC-Cr3C2 cermet coating on steel substrate

Search this article

Abstract

WC-Cr3C2 cermet coating on carbon steel was fabricated by laser controlled reactive synthesis and exhibited the metallurgical bonding at the interface between coating and substrate. The microstructure and wear properties of laser-clad WC-Cr3C2 Cermet Coating on steel substrate have been investaged by means of scaning eletron microscopy (SEM), X-ray diffraction (XRD), microhardness testing and wear testing. Experimental results show that the coating has a very good thermal resistance and high bonding strength due to Ni addition, which decreases stress concentration at the interface and increases the bonding strength due to better wettability. The coating shows superior hardness and wear resistance. In the same wear conditions, the wear resistance of the coating is 4 times than that of steel substrate.

Journal

  • MATERIALS TRANSACTIONS

    MATERIALS TRANSACTIONS 52 (3), 560-563, 2011

    The Japan Institute of Metals and Materials