Fabrication of TiC-20 mass%Ni Cermet Using MA-PCS Process
-
- Kobayashi Keizo
- Materials Research Institute for Sustainable Development, National Institute of Advanced Industrial Science and Technology
-
- Ozaki Kimihiro
- Materials Research Institute for Sustainable Development, National Institute of Advanced Industrial Science and Technology
Bibliographic Information
- Other Title
-
- Fabrication of TiC 20massパーセントNi Cermet Using MA PCS Process
Search this article
Abstract
Mechanical alloying and pulsed-current sintering were used to synthesize TiC-20 mass%Ni cermet with ultra-fine TiC particles dispersed. The mixture, in which Ti and Ni elements were uniformly distributed, was prepared by mechanical alloying of Ti, Ni and graphite powders for 18 ks. TiC particles were produced in the mixture milled for longer than 18 ks through a combustion synthesis reaction during heating. Mechanically alloyed Ti-C-Ni composite powder milled for 18 ks was consolidated using pulsed-current sintering at 1223 K under 70 MPa pressure. The sintered compact consisted of TiC and Ni. The average grain size of TiC particles in the sintered body was 0.80 μm. The relative density of the sintered compact reached 92% of the theoretical one; its Vickers hardness was 2260 Hv.
Journal
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 47 (10), 2561-2565, 2006
The Japan Institute of Metals and Materials
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390282679227373952
-
- NII Article ID
- 10018310419
-
- NII Book ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL BIB ID
- 8092244
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed